PTFE 2005

Carbon Graphite 2000

CONSTRUCTION
Style 2005 is a firm, high density interlock braided packing manufactured from pure PTFE filaments pretreated with PTFE dispersion, but contains no other lubricants. The PTFE dispersion provides a low friction surface finish and prevents leakage through the braid.

APPLICATION / SERVICE
Style 2005 is commonly used in valves and lower shaft speed applications. It is resistant to most chemicals, aggressive fluids, gases and solvents, with the exception of molten alkali metals.

SERVICE LIMITS
Types Description Value
Temperature Limits: Minimum -400°F (-200°C)
Maximum 540°F (280°C)
Pressure Limits: Rotating 290 psi (20 bar)
Reciprocating 2150 psi (150 bar)
Static 3600 psi (250 bar)
Shaft Speed: 984 fpm (5 m/s)
pH: 0-14
APPROXIMATE YIELDS (+/- 10%)
Size Feet/Pound Size Feet/Pound
1/8″ 93 1/2″ 5.2
3/16″ 41.3 9/16″ 4.3
1/4″ 21 5/8″ 3.5
5/16″ 13.7 3/4″ 2.5
3/8″   9.8 7/8″ 1.9
7/16″   7.3 1″ 1.5

Properties and application parameters shown throughout this datasheet are typical. Your specific application should not be undertaken without independent study and evaluation for suitability. For specific application recommendations consult TEADIT. Failure to select proper sealing products could result in property damage and/or serious personal injury. Specifications are subject to change without notice. This edition supersedes all previous issues.

 